銅スラグ研磨剤
DiamondCore Copper Slag
銅スラグ研磨剤 (iron silicate blasting media) are produced from granulated slag generated during metal smelting processes. The material forms hard, angular particles that provide strong cutting performance for abrasive blasting and industrial surface preparation. 結果として, copper slag abrasives effectively remove rust, ミルスケール, and old coatings from steel surfaces before coating, 絵画, or corrosion protection.
During blasting, operators propel abrasive particles toward the work surface to clean and prepare metal structures for protective coatings. 加えて, DiamondCore copper slag abrasives are used in shipyards, 鉄鋼加工工場, タンクのメンテナンス, およびインフラストラクチャプロジェクト. さらに, consistent grading and reliable blasting performance support efficient surface preparation for contractors and abrasive distributors worldwide.
Our Grit characteristics
7 grade hardness according to Moh’s scale.
Irregular prismatic shape with a lot of sharp edges, which gives great abrasiveness and kinetic energy produced by weight and speed in airstream.
Suitable for all kinds of blasting with standard equipment for that purpose.
High Blasting Efficiency
Angular particles provide strong cutting power for removing rust, ミルスケール, and old coatings.
Consistent Grading
Controlled particle size distribution ensures stable blasting performance and predictable surface profiles.
Low Free Silica
Low free silica content helps reduce health risks during abrasive blasting operations.
Reliable Industrial Supply
Stable production capacity supports large projects and international export supply.
PHYSICAL PROPERTIES
| SL# | Parameters | Analytic method | Result |
| 1 | Grain shape | – | Sharp & angular |
| 2 | Bulk Density (g/cm³) | GB/T 14684-2022 | 1.9 |
| 3 | True Density) (g/cm³) | GB/T 14684-2022 | 3.9 |
| 4 | Moh’s Hardness | GB/T 23978-2009 | 7 |
| 5 | Water Content( %) | – | 2.2 |
| 5 | Colour | – | Brownish Black |
| 6 | Salt content (calculated as NaCl)(%(w/w)) | JGJ 52-2006 | 0.025 |
| 7 | Chloride ion (Cl-) content(%(w/w)) | GB/T 176-2017 | 0.015 |
chemical composition
| SL# | 名前 | Symbol | Analytic method | Result % |
| 1 | Iron Oxide | Fe₂O₃ | GB/T 3884.7-2012 | 40-45 |
| 2 | Silicon Dioxide | SiO₂ | GB/T 3884.11-2012 | 30-35 |
| 3 | Aluminium Oxide | Al₂O₃ | GB/T 3884.12-2010 | 2-4 |
| 4 | Potassium Oxide | K₂O | GB/T 3884.9-2012 | 3-5 |
| 5 | Sodium Hydroxide | Na₂O | GB/T 3884.10-2012 | 0-2 |
| 6 | Cooper | Cu | DZG 20-2~3-2011 | 0.1-0.3 |
| 7 | Lead | Pb | DZG 20-2~3-2011 | < 1 |
| 8 | Zinc | Zn | DZG 20-2~3-2011 | 0.6-0.8 |
| 9 | Free Silica | Si | JIS A 1106 | < 1% |
DIFFERENT grit range
Based on costumer request, we are able to manufacture grit within range from
0.2 mm to 3.0 mm granulation range